Description
PHYSICAL AND MECHANICAL SPECIFICATIONS OF THE DZATA CEMENT
| Property | Common Name | Value | |
|---|---|---|---|
| Fineness (Blaine) | cm2/g | 3505 | |
| Residue | % | 9.1 | |
| Water Consistency | % | 27.22 | |
| Initial Setting Time | Minutes | 156 | Min 60 |
| Final Setting Time | Minutes | 329 | |
| 1 Day (Compressive Strength) | MPa | 20.1 | |
| 2 Day (Compressive Strength) | MPa | 35.73 | Min 20 |
| 7 Day (Compressive Strength) | MPa | 40.82 | |
| 28 Day (Compressive Strength) | MPa | 51.7 | ≥ 42.5 ≥ 62.5 |
| Soundness | mm | 0/td> | Max 10mm |
CHEMICAL SPECIFICATIONS OF THE DZATA CEMENT
| Oxide | Common Name | Unit | Value |
|---|---|---|---|
| SiO2 | Silicon Oxide | % | 19.85 |
| Al2O3 | Aluminum Oxide | % | 4.62 |
| Fe2O3 | Ferric Oxide | % | 3.92 |
| MgO | Magnesium Oxide | % | 1.04 |
| CaO | Calcium Oxide | % | 63.94 |
| SO3 | Sulfur Trioxide | % | 2.17 |
| Cl | Chloride | % | 0.05 |
| Na2O | Sodium Oxide | % | 0.31 |
| P2O5 | Phosphorus Pentoxide | % | 0.10 |
| K2O | Potassium Oxide | % | 0.16 |
| MnO3 | Mangenese Oxide | % | 0.19 |
| TOTAL | % | 99.93 | |
| I.R | Insoluble Residue | % | 1.24 |
| L.O.I | Loss on Ignition | % | 3.35 |
| Cr(Vl) | Chromium Hexavalent | ppm | 0.10 |